XSYEM02

BOPLA Film

BOPLA heat-shrinkable film

BOPLA tape film

BOPLA metallized film

BOPLA printed composite film
Biodegradable Modified Resin

XSYIM01

XSYEM01

XSYEM02

XSYBM01

XSYBM02

XSYBM03

XSYBM04
PLA Products

Straw Series

Knife, Fork, Spoon Series

Injection Series

Transparent Cup Series

Cup Lid Series

PLA Meal Box Series

Corn Starch Meal Box Series

Tray Series

Film Series

Film Bag Series

Raw Material Series

To learn more information

Please contact us further

XSYEM02

XSYEM02 is a blister-grade biodegradable resin with milky-white particles that are prone to moisture absorption and odorless. The product is processed into biodegradable sheets through extrusion and then manufactured into various blister products via blister molding. If the final products require high-temperature resistance (≧60℃), annealing treatment must be performed during the blister molding process to enhance the crystallinity of the material. The resin's food safety performance meets the relevant requirements of GB4806, and its biodegradability complies with international authoritative standards such as EN13432 and ASTM D6400.

Main ingredients

PLA, Talc Main component: PLA, Talc

Technical indicators

Mechanical properties (after complete annealing)
test project	Test Standard	unit	Test results
tensile strength	ISO 527	MPa	≥25
Elongation at break	ISO 527	%	≥10

Heat Deflection Temperature
test project	Test Standard	Unit	Test results
Before crystallization	ASTM D648-2007	°C	≤60
After crystallization	ASTM D648-2007	°C	≥80

Others
Test project	Test standard	Unit	Test results
Melt index	ISO 1133	g/10min (190℃，2.16KG)	≦10
Density	ISO 1183	g/cm3	1.30-1.35

Processing strip	Unit	Suggested value
The temperature at the rear of the barrel	℃	130-150
The temperature in the middle of the barrel	℃	175-185
The temperature at the front of the barrel	℃	175-185
Die temperature	℃	175-185
Mold temperature	℃	110
Crystallization time	s	3-10

Application field

Biodegradable lunch boxes, cups, bowls, plates, etc
Storage and Packaging

This product is made of fully biodegradable plastic particles. It should be stored in a dry and well-ventilated place, away from light, and used as soon as possible after opening the package. For particles that have not been fully used up after unpacking, they should be dried for the next use. The drying temperature should be 80℃ and the drying time should be 4 hours.